700 MPA Hard 0Cr21Al4 Resistance Heating Strip FCHW 2

Brand Name : DLX

Model Number : 0Cr21Al4

Place of Origin : China Jiangsu

MOQ : 5

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : 500 tons per month

Delivery Time : 7-20 days

Packaging Details : Spool package with Carton box, Coil package with polybag

Material : Ferrous Chromium Aluminum

Nickel(Min) : Cr 17 Al 4

Resistivity : 1.23+/-0.05

Tensile Strength : 700MPA

Elongtation : ≥12%

Application : Heating, Resistivity

Condition : Hard / Soft

Sureface : Bright, Oxided, Acide

Maximum Temperature : 1100℃

Melting Point : 1400℃

Name : resistance heating strip

Certification : CE,ROHS

Contact Now

700 MPA Hard 0Cr21Al4 Resistance Heating Strip FCHW 2

FeCrAl Series

FeCrAl alloy has the characteristic of high resistivity, low temperature resistance coefficient, high operating temperature, good anti-oxidation and anti-corrosion under high temperature.

It is widely used in industrial furnace, household appliances, metallurgy, machinery, aircraft, automotive, military and other industries producing heating elements and resistance elements.

Common Name: OhmAlloy123,FCHW-2

0Cr21Al4 resistance heating strip.

Ferrous Chromium Aluminum alloy performance tables

Alloy Nomenclature Performance		1Cr13Al4	0Cr25Al5	0Cr21Al6	0Cr23Al5	0Cr21Al4	0Cr21Al6Nb	0Cr27Al7Mo2
Main Chemical composition	Cr	12.0-15.0	23.0-26.0	19.0-22.0	20.5-23.5	18.0-21.0	21.0-23.0	26.5-27.8
	Al	4.0-6.0	4.5-6.5	5.0-7.0	4.2-5.3	3.0-4.2	5.0-7.0	6.0-7.0
	Re	opportune	opportune	opportune	opportune	opportune	opportune	opportune
	Fe	Rest	Rest	Rest	Rest	Rest	Rest	Rest
							Nb0.5	Mo1.8-2.2
Max. continuous service temp. of element(°C)		950	1250	1250	1250	1100	1350	1400
Resistivity at 20ºC(μΩ·m)		1.25	1.42	1.42	1.35	1.23	1.45	1.53
Density(g/cm3)		7.4	7.1	7.16	7.25	7.35	7.1	7.1
Thermal conductivity(KJ/m·h·ºC)		52.7	46.1	63.2	60.2	46.9	46.1
Coefficient of lines expansion(α×10-6/ºC)		15.4	16	14.7	15	13.5	16	16
Melting point approx.( ºC)		1450	1500	1500	1500	1500	1510	1520
Tensile strength(N/mm2)		580-680	630-780	630-780	630-780	600-700	650-800	680-830
Elongation at rupture(%)		>16	>12	>12	>12	>12	>12	>10
Variation of area(%)		65-75	60-75	65-75	65-75	65-75	65-75	65-75
Repeat Bending frequency(F/R)		>5	>5	>5	>5	>5	>5	>5
Hardness(H.B.)		200-260	200-260	200-260	200-260	200-260	200-260	200-260
Continuous Servicetime(Hours/ ºC)		--	≥80/1300	≥80/1300	≥80/1300	≥80/1250	≥50/1350	≥50/1350
Micrographic structure		Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite
Magnetic properties		Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic

The Form we could offer

Size Range
Wire	dia 0.03-7.5mm
	dia 8.0-12.0mm
Ribbon	(0.05-0.35)*(0.5-6.0)mm

Strip	(0.50-2.5)*(5-180)mm

Rod	8-50mm

Product Tags:

700 MPA FCHW 2

0Cr21Al4 Fecral

Resistance Heating Strip FCHW 2

700 MPA Hard 0Cr21Al4 Resistance Heating Strip FCHW 2 Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Changzhou DLX Alloy Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!